Medios Materiales.
CAST Frontlit Mesh
| Base fabric |
Polyester 1000*1000d |
Construction |
9*9 |
Thickness |
45+/-0.02 mm |
Total weight |
250+/-20 g/sqm GB 4512-1989 |
Width |
1.02-3.60 m |
Tear strength |
350/350N/5cm Warp/weft QP/T1130-1991 |
Tensilestrength |
250/250N/5cm Warp/weft GB 1040-1992 |
Welding strength |
>415 N/5cm |
Temperaturescore |
-30 - 70 'C |
Light transmission |
5% GB 2410-1980 |
Flame retardant |
<10 Mm/min Din75200/din4102 |
CAST Frontlit CB3200
| Base fabric |
Polyester 200*200d |
Construction |
12*18 |
Thickness |
0.38+/-0.02 mm |
Total weight |
400+/-20 g/sqm GB 4512-1989 |
Width |
1.02-3.20 m |
Tear strength |
150/150N/5cm Warp/weft QP/T1130-1991 |
Tensilestrength |
300/350N/5cm Warp/weft GB 1040-1992 |
Welding strength |
>380 N/5cm |
Temperaturescore |
-20-65 'C |
Light transmission |
28% GB 2410-1980 |
Flame retardant |
<10 Mm/min Din75200/din4102 |
CAST Backlit CB5010
| Base fabric |
Polyester 500*1000d |
Construction |
12*18 |
Thickness |
0.54+/-0.02 mm |
Total weight |
650+/-20 g/sqm GB 4512-1989 |
Width |
1.02-3.60 m |
Tear strength |
350/350N/5cm Warp/weft QP/T1130-1991 |
Tensilestrength |
1200/1300N/5cm Warp/weft GB 1040-1992 |
Welding strength |
>442 N/5cm |
Temperaturescore |
-20-65 'C |
Light transmission |
33.8% GB 2410-1980 |
Flame retardant |
<10 Mm/min Din75200/din4102 |
CAST Backlit CB5300
| Base fabric |
Polyester 500*300d |
Construction |
12*18 |
Thickness |
0.40+/-0.02 mm |
Total weight |
450+/-15 g/sqm GB 4512-1989 |
Width |
1.02-3.60 m |
Tear strength |
150/150N/5cm Warp/weft QP/T1130-1991 |
Tensilestrength |
500/550N/5cm Warp/weft GB 1040-1992 |
Welding strength |
>415 N/5cm |
Temperaturescore |
-20-65 'C |
Light transmission |
33.8% GB 2410-1980 |
Flame retardant |
<10 Mm/min Din75200/din4102 |
CAST Frontlit CF2200
| Base fabric |
Base fabric Polyester 200*200d |
Construction |
12*18 |
Thickness |
0.36+/-0.02 mm |
Total weight |
400+/-15 g/sqm GB 4512-1989 |
Width |
1.02-3.20 m |
Tear strength |
150/150N/5cm Warp/weft QP/T1130-1991 |
Tensilestrength |
500/550N/5cm Warp/weft GB 1040-1992 |
Welding strength |
>415 N/5cm |
Temperaturescore |
-20-65 'C |
Light transmission |
3% GB 2410-1980 |
Flame retardant |
<10 Mm/min Din75200/din4102 |
CAST Frontlit CF5300
| Base fabric |
Polyester 500*300d |
Construction |
12*18 |
Thickness |
0.40+/-0.02 mm |
Total weight |
450+/-15 g/sqm GB 4512-1989 |
Width |
1.02-3.60 m |
Tear strength |
150/150N/5cm Warp/weft QP/T1130-1991 |
Tensilestrength |
500/550N/5cm Warp/weft GB 1040-1992 |
Welding strength |
>415 N/5cm |
Temperaturescore |
-20-65 'C |
Light transmission |
33.8% GB 2410-1980 |
Flame retardant |
<10 Mm/min Din75200/din4102 |
CAST Frontlit CF5010
Base fabric |
Polyester 500*1000d |
Construction |
12*18 |
Thickness |
0.54+/-0.02 mm |
Total weight |
650+/-20 g/sqm GB 4512-1989 |
Width |
1.02-3.60 m |
Tear strength |
350/350N/5cm Warp/weft QP/T1130-1991 |
Tensilestrength |
1200/1300N/5cm Warp/weft GB 1040-1992 |
Welding strength |
>442 N/5cm |
Temperaturescore |
-20-65 'C |
Light transmission |
5% GB 2410-1980 |
Flame retardant |
<10 Mm/min Din75200/din4102 |
CAST Frontlit CF5510
| Base fabric |
Polyester 500*1000d |
Construction |
9*9 |
Thickness |
0.54+/-0.02 mm |
Total weight |
550+/-20 g/sqm GB 4512-1989 |
Width |
1.02-3.60 m |
Tear strength |
200/200N/5cm Warp/weft QP/T1130-1991 |
Tensilestrength |
800/800N/5cm Warp/weft GB 1040-1992 |
Welding strength |
>442 N/5cm |
Temperaturescore |
-20-65 'C |
Light transmission |
5% GB 2410-1980 |
Flame retardant |
<10 Mm/min Din75200/din4102 |
|
|
 |
Pagina Principal |
|
Sobre Nosotros |
|
Servicios |
|
Equipos |
|
Contáctenos |
|
Bolsa de Trabajo |
|
Accesorios y Refacciones |
|
Consumibles Para Estudios Fotograficos |
|
Consumibles Para Impresión de Gran Formato |
Equipos Digitales Nuevos |
Digital Reacondicionado |
| Frontier: 340,
350, 370. QSS: 2701, 2901, 3101. |
Análogo Reacondicionado |
| Fuji: 298,
278,
250C, 238. QSS: 1001, 1201, 1202, 1401, 1501, 1701, 1702, 1912, 2211, 613, 901. |
Conversión Análoga/Digital |
| C-Carrier |
Estaciones de Autoservicio |
| Fuji Printpix 1000 |